Aluminium Powders for Aerated Concrete
Grade,Free Al min %,Apparent density g/cc,Blaine cm²/g,D50 µm,"H₂ evolution cc (25°C, 16 min)","Wet sieve, passing 45 µm min %",Block density kg/m³,Fineness
C100,92,0.14–0.18,15000–18000,21–25,70 min,90,350–400,Fine
C80,92,0.14–0.17,13000–16000,25–27,79 min,88,400–500,Fine
C80C,92,0.14–0.17,10000–12000,33–36,70 min,79,400–500,Medium
C80S,92,0.12–0.16,12000–15000,30–33,70 min,73,400–500,Medium
C75FX,92,0.18–0.22,10000–13000,40–42,70 min,55,500–600,Coarse
CC80,92,0.16–0.20,7000–8000,50–60,65 min,54,600–700,Coarse

Aluminium Powders for AAC
Grade,Free Al min %,"Wet sieve, passing 45 µm %",D50 µm,Apparent density g/cc,Blaine cm²/g,Block density kg/m³
CO55,94,30–40,60–75,0.150–0.220,7000–11000,700–800
CO66,91,45–62,50–60,0.130–0.200,9000–11000,600–700
CO77,90,65–75,40–50,0.130–0.200,11000–13000,500–600
CO88,90,80–92,25–35,0.130–0.200,13000–17000,400–500
CO88P,90,80–92,25–35,0.130–0.200,13000–17000,400–500
CO99,90,88 min,20–30,0.140–0.200,17000–21000,350–400
CO99P,90,88 min,20–30,0.140–0.200,17000–21000,350–400
NICO99,90,90 min,15–20,0.150–0.190,17000–22000,350
NICO99P,90,90 min,15–20,0.150–0.190,17000–22000,350
CO10P,80,98 min,8–14,0.140–0.200,18000 min,300–350

Aluminium Powders for Explosives
Grade,Free Al min %,"Wet sieve, passing 45 µm %",Water coverage cm²/g,Fatty acid % max,Apparent density g/cc,D50 µm
LDS,89,86 min,5000–9000,4,0.20 ± 0.02,15–20
SDS,88,88 min,9000–12000,4,0.20 ± 0.02,13–18
LI-55,89,75–90,—,1.0,0.070–0.130,—
FL-77,89,70–90,8000 min,3.0,0.080–0.150,—
SL-77,87,85–95,8000–12000,3.0–4.0,0.120–0.160,—

"Aluminium Powders, Atomised"
Grade,Free Al min %,Sieve specification,Typical application
1030,98,10 BSS 90 min; 30 BSS 50 max,"Ferro alloys, foundry, chemical"
3060,98,30 BSS 75 min; 60 BSS 25 max,"Ferro alloys, foundry, chemical"
1000,98,30 BSS 95 min; 100 BSS 10 max,"Ferro alloys, aluminothermic, welding"
1500,98,100 BSS 95 min; 200 BSS 10 max,Brake lining
2000,98,100 BSS 90 min; 300 BSS 40 max,"Foundry, chemical, defence"
3000,98,"53 µm, 40 min passing","Slurry explosives, ammunition, refractories"
3000R,98,"53 µm, 70 min passing","Speciality refractories, pharmaceutical"
4000,98,"53 µm, 80 min passing","Speciality explosives, refractories, defence"
AT(E),98.5,+250 µm 90 min; +45 µm 5 max,"Brake linings, ferro alloys, thermit"
AT(LT),98.5,+150 µm 90 min,"Foundry fluxes, mining explosives"
AT(B),98.5,+75 µm 40–55; +45 µm 45 max,"Chemicals, sintering, pigments"
D,98,Pan 50–70 (45 µm),"Pigments, adhesives, chemicals"
DU,98,Pan 85 min (45 µm),"Abrasives, cold soldering, pigments"
DU10,98,+45 µm 5 max,Superfine dust grades

Aluminium Pellets
Grade,Form,Type,D50 µm,Carrier,Carrier % max
PEW-012,Pellet,Leafing,15–25,PE wax,15 ± 5
PEW-020,Pellet,Leafing,12–20,PE wax,15 ± 5
210-80-P,Pellet,Leafing,13 ± 2,PE wax,25
315-80-P,Pellet,Leafing,10 ± 1,PE wax,25
315-90-M,Granule,Leafing,10 ± 1,Paraffin oil,10
315-80-M,Granule,Leafing,10 ± 1,Paraffin oil,20
720-90-M,Granule,Non-leafing,85 ± 10,Paraffin oil,15